| Carrier: | PE |
|---|---|
| Color: | White |
| Certification: | RoHS, CE |
| Light and Weather Resistance: | More Than 4 |
| Melting Temperature: | 140 C-200 C |
| Melt Index (21.6kg/200 C): | 1-5g/10min |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 1. Color Masterbatch for Polyethylene/Polyethylene Masterbatch/Color Master batch for Polyethylene is made of PE and PP as carriers, inorganic pigments and organic dyes with high-performance additives. The particles are uniform and colorful in appearance, cylindrical or flat-round in shape, uniform in color, good dispersibility, stability and heat resistance. It is widely used in packaging film, pots, bottles, caps, pipes, containers, toys, household appliances, office supplies, automotive accessories and all kinds of construction. It is suitable for all kinds of blow moulding, extrusion, injection moulding, casting, wire drawing, chemical fibre and other processing fields.
2. Performance:High concentration, high brightness, uniform dispersion and strong dyeing power.
3. Application ratio:The master batch and the raw resin can be mixed evenly at the ratio of 1:25-50 (depending on the specific requirements of the product). (Note: Resin containing moisture is used after drying).
| Color Masterbatch for Polyethylene/Polyethylene Masterbatch/Color Master batch for Polyethylene | |||
| Carrier | PP PE LLDPE/LDPE/HDPE |
Induction time of oxidation OIT (200ºC) | 30-1000min |
| Pigment | Rutile titanium dioxide, Dupont titanium dioxide, Anatase titanium dioxide | Phase fusibility | PPR/PE/PP |
| Rutile titanium dioxide content | 70% | Pellets diameter (mm) | 1.8-2.8 |
| Light and weather resistance | Grade 4-8 | Density (g/cm³) | 1.2-1.6 |
| Melt index 21.6KG/200ºC | 10-30g/10min | Moisture content (%) | ≤0.05 |
| Melting point | 140ºC-220ºC | Technical Specification | SGS, FDA, RoHS, ISO9001 |