PP PE Masterbatch for Plastic Film Blowing Injection Molding

• Carrier: PP PE EVA
• Color: Colorful
• Certification: RoHS, CE
• Melting Temperature: 140 C-200 C
• Melt Index (21.6kg/200 C): 1-30/10min
• Product Application: Film Blowing, Blow Molding, Injection
• Model NO.: Film Blowing Injection Molding masterbatch
• Density(g/cm3): 2.0-2.4
• Light and Weather Resistance: Grade 4-8
• Transport Package: Paper-Plastic Composite Bags, 25kg/Bag Net Content
• Origin: China
• HS Code: 3901909000
• Production Capacity: 120000 Mt/ Year

Product Description

The master batch and the raw resin can be mixed evenly at the ratio of 1:25-50 (depending on the specific requirements of the product). (Note: Resin containing moisture is used after drying)

Performance:
High concentration, high brightness, uniform dispersion and strong dyeing power.

Proportion of application:
The master batch and the raw resin can be mixed evenly at the ratio of 1:25-50 (depending on the specific requirements of the product). (Note: Resin containing moisture is used after drying)

Physical properties:

Color Masterbatch/Masterbatch Color/Plastic Color Masterbatch
Carrier	PP PE LLDPE/LDPE/HDPE	Induction time of oxidation OIT (200ºC)	30-1000min
Pigment	Rutile titanium dioxide, Dupont titanium dioxide, Anatase titanium dioxide	Phase fusibility	PPR/PE/PP
Rutile titanium dioxide content	70%	Pellets diameter (mm)	1.8-2.8
Light and weather resistance	Grade 4-8	Density (g/cm³)	1.2-1.6
Melt index  21.6KG/200ºC	10-30g/10min	Moisture content (%)	≤0.05
Melting point	140ºC-220ºC	Technical Specification	SGS, FDA, RoHS,  ISO900